Analysis of the fragility of the Zr77Ni23 metallic glass based on low-temperature heat capacity measurements

Salčinović Fetić, Amra and Remenyi, Georgy and Starešinić, Damir and Kuršumović, Ahmed and Babić, Emil and Sulejmanović, Suada and Biljaković, Katica (2017) Analysis of the fragility of the Zr77Ni23 metallic glass based on low-temperature heat capacity measurements. Physical Review B, 96 (6). p. 64201. ISSN 1098-0121

PDF - Published Version
Language: English

Download (591kB) | Preview


We present an experimental investigation of the fragility and heat capacity of metallic glass Zr77Ni23. The ribbon sample was produced by melt-spinning technique. Glass transition temperature Tg obtained by differential scanning calorimetry with various heating rates was used to estimate fragility parameter m. Heat capacity measurements were performed in a wide temperature interval, ranging from 1.8 K up to room temperature, for as-cast and relaxed samples in different magnetic field strengths. Our results do not show any excess of vibrational density of states over the Debye contribution corresponding to the boson peak. Relaxation of the sample causes a slight decrease of Debye contribution consistent with the measured increase of Young modulus. The fact that no boson peak is observed in heat capacity, together with the obtained intermediate fragility of m=53, positions Zr77Ni23 well outside established correlations between fragility, boson peak strength, and glass forming ability.

Item Type: Article
Keywords: metallic glass, fragility, heat capacity, boson peak, glass forming ability
Date: August 2017
Subjects: NATURAL SCIENCES > Physics
Additional Information: © 2017 American Physical Society. Received 13 February 2017. Revised 4 June 2017. Published 7 August 2017.
Divisions: Faculty of Science > Department of Physics
Publisher: American Physical Society
Depositing User: Gordana Stubičan Ladešić
Date Deposited: 20 Nov 2017 18:22
Last Modified: 20 Nov 2017 18:22

Actions (login required)

View Item View Item